Eighty-eight pairs of disks (10 and 5 mm in diameter, 3 mm thickness) were prepared from heat-pressed feldspar ceramics (GC Initial IQ). After being stored in mucin-artificial saliva for 2 weeks, the 10-mm disks were divided into four surface treatment groups (n = 22) and then treated as follows: (1) no treatment (control); (2) 40% phosphoric acid; (3) 5% hydrofluoric acid + acid neutralizer + 40% phosphoric acid; (4) silica coating (CoJet-sand) + 40% phosphoric acid. The 5-mm disks were treated with 5% hydrofluoric acid + 40% phosphoric acid. The two sizes of porcelain disks, excluding the control group, were primed with Clearfil Ceramic Primer. The specimens in each group were further

divided into two subgroups of 11 each, and bonded with Clearfil Esthetic Cement (CEC) or Panavia F 2.0 Cement (PFC). The specimens were Ku-0059436 ic50 stored in distilled water at 37°C for 24 hours, thermocycled for 3000 cycles at 5 to 55°C, and stored at 37°C for an additional 7 days. Shear bond strength (SBS) was measured with a universal testing machine at a 0.5 mm/min

crosshead speed until fracture. Statistical analysis of the results was carried out with a two-way ANOVA and Tukey HSD test (α = 0.05). Debonded specimen surfaces were examined under an optical www.selleckchem.com/products/azd9291.html microscope to determine the mode of failure. The statistical analysis showed that the SBS was significantly affected by surface treatment and resin cement (p < 0.05). For treatment groups bonded with CEC, the SBS (MPa) values were (1) 2.64 ± 1.1, (2) 13.31 ± 3.6, (3) 18.88 ± 2.6, (4) 14.27 ± 2.7, while for treatment groups cemented with PFC, the SBS (MPa) values were (1) selleck 3.04 ± 1.1, (2) 16.44 ± 3.3, (3) 20.52 ± 2.2, and (4) 16.24 ± 2.9. All control specimens exhibited adhesive failures, while mixed types of failures were observed in phosphoric acid-treated groups. The other groups revealed mainly cohesive and mixed failures. Combined surface treatment of etching with hydrofluoric acid and phosphoric acid provides the highest bond strengths to porcelain. Also, PFC exhibited higher SBS than

CEC did. “
“The aim of this study was to determine the survival rates over time of implant-supported ceramic–ceramic and metal–ceramic prostheses as a function of core-veneer thickness ratio, gingival connector embrasure design, and connector height. An IRB-approved, randomized, controlled clinical trial was conducted as a single-blind pilot study involving 55 patients missing three teeth in either one or two posterior areas. These patients (34 women; 21 men; age range 52–75 years) were recruited for the study to receive a three-unit implant-supported fixed dental prosthesis (FDP). Two implants were placed for each of the 72 FDPs in the study. The implants (Osseospeed, Astra Tech), which were made of titanium, were grit blasted. A gold-shaded, custom-milled titanium abutment (Atlantis, Astra Tech), was secured to each implant body.